Dr. Dmitri Kopeliovich

Low viscosity oils produce less friction and therefore decrease the fuel consumption and combustion gas emissions.

One of the consequences though of lowering oil viscosity is a decrease of the minimum oil film thickness. The shaft surface is getting closer to the bearing surface.
This increases the failure threat level of such factors as surface roughness, shaft grinding irregularities, oil borne foreign particles and geometrical distortions and misalignments.
Direct metal-to-metal intermittent contact between the surfaces occurs more frequently.
The wear rate is increased due to the direct metal-to-metal contact.
In this case seizure resistance of the bearing material becomes more important.

The lead based overlay of the conventional tri-metal bearing has a very good seizure resistance, and if the misalignments, shaft grinding defects, etc. are very small, a tri-metal bearing will work perfectly with low viscosity lubricant.
However if the dimension of the geometrical defect is close to the overlay thickness (0.0008”/0.020mm), the overlay is worn fast in some bearing areas and the intermediate layer is exposed.
The intermediate layer has some level of emergency seizure resistance but this level is definitely insufficient for normal bearing operation.

The AlSnSi bearings are much more tolerant to the geometrical defects due to the large thickness of the bearing alloy (~0.01”/0.25mm).
Very good seizure resistance of AlSi alloy is achieved due to the hard silicon particles, which continuously polish the shaft surface and therefore prevent seizure.

Another problem of low viscosity oils is associated with the distribution of oil pressure over the bearing surface.
Oil viscosity does not exert influence on the average pressure however it does affect the value of the pressure peak. The pressure distribution in low viscosity oil is less uniform – the peak pressure is higher therefore the load applied to the bearing material in this particular area is higher.
This may cause fatigue if the fatigue strength of the material is insufficient.
The effect of low viscosity oil on the pressure distribution may be compensated by a decrease of the bearing clearance.

to top

• Bearings in internal combustion engines
• Engine parameters determining bearing loading
• Lubrication regimes
• Hydrodynamic journal bearing
• Hydrodynamic lubrication theory
• Geometrical parameters of engine bearings
• Mechanisms of wear
• Requirements to engine bearing materials
• Engine bearing fatigue test
• Engine bearing materials
• Copper based bearing materials
• Manufacturing bi-metal strips for copper bearings
• Aluminum based bearing materials
• Continuous casting of aluminum based bearing alloys
• Manufacturing bi-metal strips for aluminum bearings
• Lead based engine bearing overlays
• Tin based engine bearing overlays
• Sputter bearing overlays
• Polymer based engine bearing overlays
• Engine bearing failure
• Selection of engine bearing materials
• pMax Black™ - Strengthened Tri-metal Bearing Materials for High Performance Bearings
• U-Groove™ Modified Design of Oil Groove for High Performance Bearings
• ElliptiX™ Oil Hole of New Design for High Performance Bearings
• EccentriX™ Optimal Eccentricity for High Performance Bearings
• RadiaLock™ - Design of Crush Height for Reliable Press Fit of High Performance Bearings
• Modern Trends In Materials For High Performance Engine Bearings
• Optimization of Clearance Design for High Performance Engine Bearings
• Camshaft Bearings
• Ecological Aspects Of Engine Bearings
• Consistency in Bearing Wall Thickness
• Soft Strength of Racing Bearings
• Effect of oil viscosity on hydrodynamic friction of engine bearings
• Bearing Materials For Race Engines
• Oil Clearance and Engine Bearings
• Polymer Coated Bearings
• Development of Performance Bearings for Race Engines of Modern Design
• Failures of Engine Bearings and their Prevention
• Engine Bearing Housing and How it Affects Engine Bearings
• Polymer Coatings for Race Engine Bearings
• Heavy Duty Engine Bearings - Materials, Geometry, Failures
• Hydrodynamic Bearing – Calculations and Design
• Geometry of Engine Bearings
• Crush Height of Engine Bearings
• Materials for Engine Bearings
• Engine oils

to Metals
to Engine bearings